| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 105 - 123 |
| Density | g mL-1 | 0.90 - 0.92 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 2.0 |
| Heat Deflection Temperature, 0.5 MPa | °C | 43 - 55 |
| Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | |
| Thermal Conductivity | W / mK | 0.35 |
| Shore Hardness, D Scale | n/a | 45 - 55 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 7.0 - 16 |
| Tensile Strength, Break at 23 C | MPa | 32 - 60 |
| Elongation, Yield | % | 200 - 750 |
| Elongation, Break | % | 450 - 810 |
| Tensile Modulus at 23 C | MPa | 120- 550 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | |
| Compressive Strength | MPa | |
| Izod Notched | J/m (kJ/m2) | 475 |
| Izod Unnotched | J/m | No Break |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | 6 x 1015 | |
| Dielectric Strength | V/mm x 104 | 1.9 - 3.5 | |
| Dielectric Constant @ 1 MHz | n/a | 2.2 - 2.4 | |
| Dissipation Factor @ 1 MHz | n/a | 0.0001 - 0.0005 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 160 - 200 | |
| Linear Mold Shrinkage | cm/cm | 0.017 | |
| Continuous Service Temperature | °C | 40 - 70 | |
| Water Absorption, 24 hr. Immersion | % | 0.01 - 0.03 |